Abstract
Ni3Al-based single crystal alloy IC6SX with different crystal orientations were prepared by seed crystal method. The microstructure and heat treatment of the alloy were investigated. The results showed that the microstructure of the alloy was in dendrite structure, and the crystal orientation had significant effect on the dendrite morphology of this alloy. The precipitated phases of (MoNi)6C and NiMo appeared in the microstructure of the three alloys with different crystal orientations during solidification process. Compared with other two alloys, the volume fractions of precipitated phases of both (MoNi)6C and NiMo was the most in the alloy with [111] orientation and the least in the alloy with [001] orientation. The solidus and liquidus temperatures of the alloy IC6SX tested by differential scanning calorimetry (DSC) were 1356 °C and 1387 °C, respectively. Meanwhile, the effect of different solution temperatures on the microstructure of the alloy with different orientations was studied. The results showed that the precipitated phases of (MoNi)6C and NiMo were eliminated with the solid solution treatment under the condition of 1300 °C/10 h. However, the incipient melting of the alloys occurred due to the dissolution of low melting point phases. As the temperature dropped to 1280 °C, the area of incipient melting in the alloy with different orientations decreased gradually. However, there was no incipient melting appearing in the three alloys with different orientations when the solution treatment temperature dropped to 1260 °C.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call