Abstract
The microstructure and mechanical properties of Sn–xBi (x = 10, 20, 25, and 35) solder alloy were investigated by scanning electronic microscope and notch tensile test. The results showed that the microstructure of Sn–10Bi and Sn–20Bi solder alloy was constituted by Bi particle and β-Sn phase. The microstructure of Sn–25Bi and Sn–35Bi solder alloy was consisted of eutectic phase and primary phase. The ultimate tensile load of Sn–20Bi solder alloy was higher than that of Sn–10Bi in notch tensile test. The ultimate tensile load of Sn–25Bi and Sn–35Bi was declined gradually compared with that of Sn–20Bi solder alloy. The fracture energy of Sn–xBi was decreased continuously when the Bi fraction increased. Crack observation, fracture surface observation, and finite element analysis revealed that the crack initiation and propagation of Sn–25Bi and Sn–35Bi was dominated by the fracture of brittle eutectic phase. Therefore, the ultimate tensile load and fracture energy of Sn–25Bi and Sn–35Bi were damaged compared with that of Sn–20Bi.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.