Abstract
In this paper, t mol% Nb2O5 doped x(Ba0.7Ca0.3)TiO3–(1−x)Ba(Zr0.2Ti0.8)O3 [xBCT–(1−x)BZT–t mol% Nb2O5] lead-free piezoelectric ceramics were prepared successfully using a solid-state reaction technique. Firstly, the phase transition of xBCT–(1−x)BZT ceramics were investigated, and it was found that 0.47BCT–0.53BZT sample shows a rhombohedral (R)–tetragonal (T) phase transition at room temperature near Morphotropic Phase Boundary and presents better ferroelectric and piezoelectric properties compared with the other component ceramics. On this basis, the crystal structure, surface morphologies and electrical properties of the Nb2O5 doped 0.47BCT–0.53BZT ceramic were studied in detail. It was found the grain size increases monotonously and the microstructure become more denser and homogeneous when Nb-doping concentration increases above t = 0.3, and a maximum strain value of 0.132% was obtained at E = 20 kV/cm. Additionally, the excellent electric properties with a high remanent polarization (Pr = 8.3 μC/cm2), a low coercive field (Ec = 1.55 kV/cm) were also obtained on 0.47BCT–0.53BZT–0.3 mol% Nb2O5 lead-free ceramics, which is promising for application in lead-free practical applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.