Microstructure and Compression Behavior of Ti3Al Based Ti-Al-V Ternary Alloys

Abstract

AbstractThe ordered alloy phase of Ti3Al shows a rather wide solid solution range in aluminum and also in vanadium. Several Ti-Al-V ternary alloys have been prepared to investigate the alloy composition effect upon microstructure, crystallography, and mechanical characteristics. The materials containing 75, 70, and 65 at.% titanium, and 0 or 5 at.% vanadium were prepared by arc melting. Metallographic observation has revealed that the binary Ti-Al alloys contained somewhat coarse grains with about 100 μm grain diameter. In contrast to this, ternary alloys containing 5 at.% vanadium showed smaller grained microstructures with grain diameters around 15 μm. The grain size could not be adjusted to a unified value in the present study. X-ray diffraction study and microanalysis showed that the alloys contained single phase α2. Not every possible diffraction peak of the D019 ordered structure has been observed in the XRD patterns. The lattice parameters, a and c, were observed to decrease as the aluminum content increased and also when vanadium was added. Compression tests have been performed at various temperature ranging from an ambient temperature up to 1300K on rectangular parallelepiped specimens with 2mm×2mm×3mm dimensions. Alloys containing more aluminum showed higher strength, and vanadium addition enhanced the strength of the alloys. In some alloys deformability and strength are both enhanced by vanadium addition in some alloys. Temperature dependence of strength showed a little variation upon chemical compositions.