Abstract
The effect of alkali pre-treatment (sodium hydroxide, NaOH) on the microstructural, mechanical, and chemical composition of oil palm stalk fibres (OPSF) is reported for future bioconversion processes. The OPSF was pre-treated with various concentrations of NaOH (5, 10, 20, 30, and 40% w/v). Scanning electron microscopy analysis revealed that 5% w/v alkali concentration caused complete removal of silica bodies and waxy layers, whereas pronounced degradation of the fibres occurred at 40% w/v NaOH concentration. Mechanical test results showed that the maximum elastic modulus of untreated OPSF was 2.5 GPa and the modulus was not sensitive to alkali concentration. Permanent set (plastic strain) and viscoelastic behaviours of OPSF were observed from the loading-unloading and stress relaxation test results, respectively. Agreement was observed between the Prony series viscoelastic model and test results, which provided further evidence of the viscoelastic behaviour of OPSF.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.