Abstract

AbstractSodium bismuth titanate (Na0.5Bi0.5TiO3: NBT) a lead free piezoelectric; exhibits promising features such that it could be an alternate to lead based piezoelectrics. In this work, we report the microstructural influence on piezoelectric and leakage current behavior of NBT thin films grown by pulsed laser ablation (PLD). Various microstructural features like coarse faceted grains and fine spherical grains was achieved by effective optimization of substrate temperature and oxygen partial pressures. The studies reveals that, leakage current of NBT thin films were dominated by interface limited modified Schottky emission type of conduction. The piezoelectric domain studies reveal that for NBT thin films with fine spherical grain the domain pattern was highly dominated by the morphology and in the case of coarse faceted grains the domains were relatively large and the domains were extending beyond the grain boundaries.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.