Abstract
Abstract The effect of annealing temperature in the range from 1000 to 1200 °C on the pitting corrosion behavior of duplex stainless steel UNS S32304 was investigated by the potentiodynamic polarization and potentiostatic critical pitting temperature techniques. The microstructural evolution and pit morphologies were studied using a scanning electron microscopy with energy dispersive X-ray spectroscopy. The results demonstrated that the nucleation of metastable pits transformed from austenite phase to ferrite phase with the increasing annealing temperature. As the annealing temperature increased, the pitting corrosion resistance firstly increased and then decreased. The highest pitting corrosion resistance was obtained at 1080 °C with the highest critical pitting temperature value and pitting nucleation resistance. The results could be well explained by the microstructural evolution of ferrite and austenite phases induced by annealing treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.