Microstructural Evaluation of Tungsten Carbide-Cobalt (WC-17Co) Alloy Deposited by Cold Spraying, High Velocity Air Fuel, and High Velocity Oxygen Fuel Spraying Technologies

Abstract

Abstract In this study, microstructural characterization is conducted on WC-17Co coatings produced via High Velocity Oxygen Fuel (HVOF), High Velocity Air Fuel (HVAF), and Cold Spraying (CS). All coatings prepared were observed to be of good quality and with relatively low porosity content. SEM study showed important microstructural features and grain morphologies of each coating. While composition of feedstock material was approximately similar, elemental composition using EDS showed higher Co content and lower WC in the CS deposited coating. XRD experiment identified formation of more complex oxides and tungsten phases in coatings deposited technologies involving melting of powders such as HVOF and HVAF. These phases consisted mainly of cobalt oxides and brittle phases such as W3Co3C or W2C caused by decarburization of the tungsten carbide particles. Hardness of all coating samples were examined and CS deposited coating exhibited considerably lower hardness compared to the other two coating samples instead of having significantly lower porosity content. It could be contributed to dissociation and physical loss of hard carbide phase during high velocity impact of particles in CS process. It is in good agreement with detection of higher amount of cobalt in CS deposited coating material. It is strongly believed that results obtained from this study can be used for future investigation in thermo-mechanical properties of WC-Co coatings.