Abstract
Abstract 15 mm thick ultra-high strength steel plates with 960MPa yield strength were welded using different multi-pass laying techniques (i.e., stringer and weaving beads) with torch manipulation. Weld metals obtained were compared using different mechanical (i.e., micro tensile tests and Vickers hardness maps) and microstructural (i.e., optical microscope, scanning electron microscope, X-ray diffraction, electron backscatter diffraction) characterization techniques. Coarser grains and acicular ferrite were observed in weld metal obtained with weaving pass procedure. There were hardness differences in face and root passes of both weld metals. Yet, hardness values were 19% and 11% higher for face and root regions of the joint obtained by stringer pass procedure, respectively. Fractographs of micro tensile test specimens revealed dimples depicting ductile network structure for both joints.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.