Abstract
AbstractInterconnect coatings are extremely important to ensure an optimal performance of a solid oxide fuel cell (SOFC) stack. Nowadays the most common material used to produce SOFC interconnects is a ferritic stainless steel (FSS) rich in chromium which is much less expensive than the previously used ceramic interconnects. Nevertheless interconnects have to be coated in order to provide protection from the aggressive environment that surrounds them and reduce chromium species migration to the cell's cathode. In this work three different coatings were applied to Crofer® 22 H substrates via atmospheric plasma spraying (APS): two different stoichiometries of copper manganese oxide (CuxMn3–xO4, where x = 1.4 and 1.5) and one of cobalt manganese oxide (CoxMn3–xO4, where x = 1.5), considered the state of the art coating for SOFC interconnects. X‐ray diffraction (XRD) was used to check the composition of deposited layers. Area specific resistance (ASR) of samples has been characterized for different samples in the range 673–1,073 K and during a 100 hours ageing test at 1,073 K. Microstructural changes and Cr‐barrier properties have been characterized by SEM‐EDX analyses.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.