Microstructural Analysis of Ti/Ni Bilayer Ohmic Contacts on 4H-SiC Layers

Abstract

The micro-structural analysis of Ti/Ni bilayer as Ohmic contacts to n-type 4H-SiC is reported. There was no carbon segregation at the interface between the NiSi layer and the 4H-SiC layer for Ti/Ni contacts, unlike pure Ni contacts. The diffraction pattern image shows the presence of the cubic NiSi film which grows on the SiC surface. The film interface with the SiC was uniform and more planar. An optimized contact in terms of contact morphology was achieved using a bilayer contact Ti/Ni (20/100nm) annealed at 1100 °C for 5 minutes in vacuum.