Abstract
We report micropatterned polystyrene-clay nanocomposite (PCN) surfaces with concavities by moisture-induced phase separation of PCN particles. Micropatterned film with concavity size of 800 nm to 1.3 microm and a high number density of 2 x 10(8) features/cm(2) was obtained by drop-casting PCN solution (20 mg/mL PCN/THF) under ambient relative humidity of 70-80%. It is proposed that water droplets were channeled through the hydrophilic interfaces between the PCN particles, and the two-dimensional array of concavities was formed by spontaneous phase separation due to the presence of rigid clay platelets. The concavity size and number density can be tuned by varying the solvent for PCN. Micropatterned film with concavity size in the range of 650 nm to 1.1 microm with a number density of 5 x 10(7) features/cm(2) was obtained using chloroform as solvent, whereas a concavity size of 150-740 nm and number density of 10(8) features/cm(2) were obtained using carbon disulfide.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.