Abstract
Polystyrene-clay nanocomposite (PCN) particles, which exhibited concentration dependent self-assembling property in THF were synthesized by in situ intercalative polymerization of styrene with vinyl POSS amine-modified organoclay. While the particles from dilute solution of 0.001 mg mL(-1) showed a lateral dimension of 190-800 nm and thickness of 120 nm, microvesicles of diameter of 2.5-3.5 microm and average membrane thickness of 85 nm were produced from solution concentration of 2.5 mg mL(-1) by consuming the particles. The particle possessed a sandwich structure consisting of polystyrene(PS)-POSS-intercalated clay tactoid of thickness of 12.6 nm at the core and PS chains growing from the tactoid surfaces on either side, exposing the hydroxylated edges of the silicate layers. Vesicle was formed by edge-edge association of the silicate layers so that the layers lie flat along the vesicle membrane. Guest-encapsulated vesicles were obtained when prepared from solutions containing guest molecules.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.