Abstract
Texture evolution in TiAl depends on the type of deformation such as uniaxial compression, tension or rolling as well as on the initial microstructure. Cast TiAl shows a lamellar microstructure with an alignment of the lamellae and exhibits a strong texture. Deformation parallel to the aligned lamellae results in a plane-strain deformation which leads to a brass type texture. From room temperature up to 700 °C, compression tests of TiAl specimens with equiaxed microstructures result in <110>-fiber textures where the <101> component is shifted to <302>. At higher temperatures the orientation <302> is caused by dynamic recrystallization. In rolled sheets of TiAl with equiaxed microstructure the main texture component is a modified cube texture {100}<010> where the tetragonal c-axis is aligned in transverse direction of the sheet. This texture component is caused by dynamic recrystallization and appears to be stable against further rolling.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call