Abstract
Introduction:Bioactive endodontic sealers have been developed to improve the quality of root canal obturation. EndoSequence Bioceramic (BC) Sealer is amongst calcium silicate-based materials recently developed for permanent root canal filling. The objective of this study was to evaluate the bioactivity of BC Sealer and its micro push-out bond strength to dentin compared to AH-Plus (AH) sealer. Methods and Materials:To perform the micro push-out test, 24 root canals of mandibular premolars were instrumented and divided into two groups (n=12). Each root was cut into 4 slices and lumens of the canals were filled with the sealers and submitted to micro push-out test. Failure mode was assessed using scanning electron microscopy (SEM). Bioactivity of BC sealer was investigated with scanning electron microscopy/energy-dispersive X-ray (SEM/EDS) and X-ray diffraction (XRD). Bioactivity assessments were reported descriptively. Bond strength data were analyzed by parametric t-test (α=5%). Results:In micro push-out test AH had higher bond strength mean values (16.29 MPa) than BC sealer (9.48 MPa) (P<0.05). Both groups had low amount of adhesive failure. SEM showed the presence of a mineral precipitate after 30 days and EDS analysis showed that those precipitates have high proportion of Ca. XRD showed peaks of crystalline phases of calcium carbonate compatible with the bioactivity.Conclusion:BC sealer showed indications of bioactivity and lower bond strength to dentine compared to AH.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call