Abstract
Unsaturated polyester is the polymer material most widely used for matrix composites in the field of construction engineering, including for ships, automotive components and other engineering fields. The weakness of this polymer is that it is brittle and brittle and is unable to withstand cracking loads due to having cross-linked molecules that easily link together. The study to improve it was mixing with vinyl ester which succeeded in making the polyester crack resistant which was tested using a CTM machine and the fracture was observed using an SEM microscope. The test results showed that the polyester polymer mixed with 30% vinyl ester showed the highest increase in fracture strength, which was equal to K<sub>1c</sub> = 1.67 N.mm<sup>0.5</sup> compared to pure polyester, only K<sub>1c</sub> = 0.77 N.mm<sup>0.5</sup> can increase (216 %). Increasing the mixture content of 30% vinyl ester in polyester will change the brittle nature of unsaturated polyester to become more resilient because the vinyl ester molecules break the bonds of the polyester molecular chains.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: American Journal of Materials Synthesis and Processing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.