Abstract
Mesoporous Mn-doped Co3O4 catalysts were successfully prepared via a dry soft reactive grinding method based on solid state reaction, and their catalytic performances on CO oxidation were evaluated at a high space velocity of 49,500 mL g−1 h−1. A significant promoted effect was observed once the atomic ratios of Mn/(Co+Mn) were lower than 10%, for instance, the temperature for 50% conversion decreased to about −60 °C, showing superior catalytic performance compared to the single metal oxide. Especially, the Mn-promoted Co3O4 catalyst with a Mn/(Co+Mn) molar ratio of 10% could convert 100% CO after 3000 min of time-on-steam without any deactivation at room temperature. As prepared catalysts were characterized by XRD, N2-adsorption/desorption, TEM, H2-TPR, O2-TPD and CO-titration analysis. The significant enhancement of performance for oxidation of CO over Mn-Co-O mixed oxides was associated with the high active oxygen species concentrations formed during the pretreatment in O2 atmosphere.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.