Abstract
Alginate particles, crosslinked by calcium ions, have a number of potential biopharmaceutical industry applications due to the biocompatibility of the materials used and formed. One such use is as microcarriers for cell attachment, growth and then detachment without the use of proteolytic enzymes. A straightforward and reproducible method for producing uniform calcium alginate particles with controllable median diameters which employs membrane emulsification and internal gelation (solid particles contained in the dispersed phase) is demonstrated, as well as functionalisation of the resulting beads with amine terminated poly N-isopropylacrylamide (pNIPAM) to form temperature responsive particles, by taking advantage of the electrostatic interaction between the carboxyl groups of the alginate and amino groups of the modified pNIPAM. Cell attachment, growth and detachment capabilities of these core–shell structures were assessed and successfully demonstrated by using phase contrast microscopy and fluorescent staining with calcein-AM and ethidium homodimer-1.The formulation used for the alginate particles avoided non-GRAS chemicals by only using food grade and pharmaceutical grade reagents. The median particle size was controllable within the range between 55μm and 690μm and the size distributions produced were very narrow: ‘span’ values as low as 0.2. When using a membrane pore size of 20μm no membrane blockage by the suspended calcium carbonate necessary for internal gelation of the alginate particles was observed. Membrane pore openings with diameters of 5 and 10μm were also tested, but blocked with the 2.3μm median diameter calcium carbonate solids.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.