Abstract
Melting and solidification behaviour of lead particles of size about 30 nm has been studied in amorphous and quasicrystalline matrices of an Al75Cu15V10 alloy. The lead particles had semi-shperical morphology, and often showed twinning. The particles showed a depression in the melting temperature by about 17°C in the amorphous matrix and about 6°C in the quasicrystalline matrix, as compared to the bulk melting temperature. On solidification an undercooling of greater than 60°C is obtained. The lowering of the melting temperature and a high undercooling on solidification is qualitatively explained to be due to the interfacial energies of the liquid or solid lead with the matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.