Abstract
AbstractThe mechanism of damage accumulation and failure in thin sheets of an orthotropic long discontinued glass fiber reinforced polypropylene composite was studied using optical and electron microscopy coupled with acoustic emission (AE) monitoring. The effect of strain rate (0.1 to 100 percent) was investigated, and a close correspondence was established between AE response and microscopic observations. Furthermore, simultaneous AE monitoring and optical microscopy performed during sample deformation substantiated the assignment of certain AE amplitude ranges with specific failure events in the composite. Specifically, the failure process was found to be very inhomogeneous in nature, and could be divided into three main stages of damage accumulation. Finally, cumulative AE energy curves were found to follow an interesting powerlaw behavior. Results based on the coupling of AE methods with optical and electron microscopy were found to be self consistent and in agreement with previous reports on thicker‐section composites manufactured from the same materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.