Abstract
The influence of aging (T6 at 150°C and175°C, T8 at 150°C) and 0.72% Zn addition on the mechanical properties, microstructures and intergranular corrosion (IGC) behavior of Al-2.7Cu-1.7Li-0.3Mg alloys was investigated. With 0.72% Zn addition, the strength of the Al-Li alloy was increased. As the aging time was extended, the corrosion type of the studied Al-Li alloys was changed in the following order: pitting, local IGC, general IGC, local IGC and pitting again. For the T6 temper, as the aging temperature was elevated from 150°C to 175°C, the aging time period for IGC appearance was shortened. The pre-deformation before aging (T8 temper) also greatly shorten the aging time period for IGC. Meanwhile, the addition of 0.72% Zn decreased the IGC sensitivity and shortened the aging time period for IGC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.