Abstract
AbstractThere is a technological need for hard thin films with high elastic modulus and fracture toughness. Silicon carbide (SiC) fulfills such requirements for a variety of applications at high temperatures and for high-wear MEMS. A detailed study of the mechanical properties of single crystal and polycrystalline 3C-SiC films grown on Si substrates was performed by means of nanoindentation using a Berkovich diamond tip. The thickness of both the single and polycrystalline SiC films was around 1-2 μm. Under indentation loads below 500 μN both films exhibit Hertzian elastic contact without plastic deformation. The polycrystalline SiC films have an elastic modulus of 457 GPa and hardness of 33.5 GPa, while the single crystalline SiC films elastic modulus and hardness were measured to be 433 GPa and 31.2 GPa, respectively. These results indicate that polycrystalline SiC thin films are more attractive for MEMS applications when compared with the single crystal 3C-SiC, which is promising since growing single crystal 3C-SiC films is more challenging.
Submitted Version (
Free)
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call