Abstract
Purpose This paper aims to evaluate the mechanical properties and slurry erosion behaviour of 10TiO2-Cr2O3 coated turbine steel. Design/methodology/approach Slurry erosion experiments were performed on the coated turbine steel specimens using slurry erosion test rig under accelerated conditions such as rotational speed, average particle size and slurry concentration. Surface roughness tester, Vickers microhardness tester and scanning electron microscope were used to analyse erosion mechanism. Findings Under all experimental conditions, 10TiO2-Cr2O3 coated steel showed better slurry erosion resistance in comparison with Al2O3 coated and uncoated steel specimens. Each experimental condition indicated a significant effect on the erosion rate of both coatings and uncoated steel. The surface analysis of uncoated eroded specimen revealed that plastic deformation, ploughing and deep craters formation were the reasons for mass loss, whereas microchipping, ploughing and microcutting were the reasons for mass loss of coated specimens. Originality/value The present investigation provides novel insight into the comparative slurry erosion performance of high velocity oxy fuel deposited 10TiO2-Cr2O3 and Cr2O3 coatings under various environmental conditions. To form modified powder, 10 Wt.% TiO2 was added to 90 Wt.% Cr2O3.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.