Abstract
The goal of this study was to test the mechanical strength of 4 different cross pins currently available for femoral fixation by loading each cross pin to failure as received and determine the effect of 1 million cycles of fatigue loading. Additionally, the strength of resorbable pins was tested after prolonged exposure to biologic conditions. Six implants each of the Arthrotek LactoSorb (Biomet, Warsaw, Indiana), Mitek RigidFix (DePuy Mitek Inc, Raynham, Massachusetts), Arthrotek Bone Mulch Screw (Biomet), cortical allograft, and control were tested for 3-point failure without prior loading and after cyclic loading between 50 to 200 N at 10 Hz for 1 million cycles. The bioabsorbable pins were placed in sterile water at 37°C and tested after 2, 4, and 6 months for 3-point failure strength. All implants tested without antecedent loading demonstrated adequate strength for initial fixation for hamstring grafts. During fatigue testing, RigidFix implants (n=6) failed at 18,893±8365 cycles (with a central deformation of 0.48±0.11 mm prior to fracture). All of the other implants tested endured 1 million cycles of loading (50-200 N) without fracture or 1.5 mm central deformation. Neither of the bioabsorbable pins demonstrated a significant change in yield strength after prolonged exposure to water. All implants tested demonstrated adequate strength for initial fixation of hamstring grafts. The metal and bone implants far exceed the strength required to sustain mechanical fixation until biological fixation occurs; both polymeric implants demonstrated that they maintained enough mechanical strength to achieve this goal.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call