Abstract
This study aims to look for the best concentration of nanohydroxyapatite (NHA) and polyhexamethylene biguanide (PHMB) incorporated into glass ionomer cement (GIC) in accordance with ISO:9917-1 and evaluate its mechanical, antibacterial, biocompatible and microleakages properties. NHA was incorporated into Fuji Ⅱ GIC powder at 0-8.00 wt% concentration and specimens were prepared; the best concentration was sifted out according to ISO9917-1. Based on best NHA proportion, 0-0.80% PHMB was dispersed into powder and samples were respectively prepared. Mechanical properties include net setting time (ST), compressive strength (CS), microhardness (VNH), solubility and scanning electron microscopy (SEM) observation. Those met ISO standard were qualified to continue microleakage observation, antibacterial activity, and biocompatibility test. The results suggested that GIC/6%NHA/0.2% PHMB and GIC/6%NHA/0.4%PHMB showed great performances in mechanical, antibacterial, and microleakage improvements, and the cytotoxicity of modified GIC showed no statistical difference with pure GIC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.