Mapping the cyclic plastic zone to elucidate the mechanisms of crack tip deformation in bulk metallic glasses

Abstract

Developing damage-tolerant bulk metallic glasses (BMGs) requires knowledge of the physical mechanisms governing crack propagation. While fractography suggests that fatigue crack propagation occurs in an incremental manner, conclusive evidence of alternating crack tip blunting and resharpening is lacking. By mapping the strain fields in both the monotonic and cyclic plastic zones, it is shown that the characteristic compressive stresses required to resharpen the crack tip are developed in a BMG upon unloading. This result confirms the mechanism of fatigue crack propagation in BMGs. Broader implications of these findings are that the effect of shear banding is rather diffuse and plastic deformation ahead of a stress concentration, such as a crack tip, appears to extend well beyond the extent of visible shear bands on the sample surface.