Abstract
Decarburization tests of high-carbon ferromanganese melts by oxygen refining were successfully carried out in a model converter with 2-ton production capacity. During the oxygen refining, the manganese loss was inherently accompanied by oxidation and evaporation. The oxidation loss of manganese into slag was affected by slag composition, melt temperature and slag weight. The oxidation loss of manganese into slag was minimum at a slag basicity of about 1.5 and it increased with temperature and slag weight. The amount of manganese evaporation loss was comparable to that of oxidation loss. An empirical equation for the evaporation loss of manganese was derived as a function of process variables. The apparent vaporization coefficient, β, was significantly affected by the oxygen mixing ratio in bottom blowing gas and the fraction of top blown oxygen.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.