Abstract
Heusler alloys with nominal composition Ni73−xFexGa27 (x = 17, 18, 19, 20, 21, 22) were prepared by arc melting and subsequent homogenization by annealing. The magnetic properties of the alloys were studied to analyse the magnetic entropy change as a function of temperature. The maximum entropy change was observed in the alloy (x = 19) where martensite–austenite structural and ferro–para magnetic transitions were very close to each other. The transport properties and magnetoresistance (MR) of the samples were also investigated up to a magnetic field of 8 T and within a temperature range 4.2–325 K. It was observed that the MR in the austenite state was higher than that of the martensite state irrespective of the composition of the sample. A large negative MR (∼9% at 8 T) was obtained for the sample Ni54Fe19Ga27 at 300 K which was very close to the martensitic transition temperature as well as the Curie temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.