Abstract
We report the observation of contrasting magnetic behavior in cobalt ferrite (CFO) thin films deposited on single crystalline magnesium oxide (MgO) and strontium titanate (STO). Epitaxial films on MgO (100) with a lattice mismatch of 0.35% showed out-of-plane anisotropy whereas the films on STO (100) with a lattice mismatch of 7.4% displayed in-plane anisotropy. Stress anisotropy calculated from angle-dependent x-ray diffraction analysis confirmed that the change in anisotropy originates from the lattice mismatch. An additional low-field switching characteristic is observed in the M-H loops of the CFO films, which became prominent with lowering temperature as also evidenced from the rf transverse susceptibility measurements. The obtained results revealed that the low field switching is associated with the film-substrate interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.