Abstract

The crystallization behaviour of Fe 70.8 Nb 3.7 Cu 1 Al 2.7 Mn 0.7 Si 13.5 B 7.6 alloy prepared in the form of amorphous ribbons by melt-spinning technique was studied using differential scanning calorimetry and the temperature variation in resistivity. An X-ray diffaction and transmission electron microscopy study showed the formation of f-Fe(Si, Al) and/or Fe 3 (Si, Al) nanoparticles after the first stage of crystallization. The activation energy for this nanophase formation was 68 kcal mol m1 . The brittleness of the alloy increased with the formation of nanoparticles after heat treatment. Superior soft magnetic properties were achieved when the material was heat treated at 790 K for 15 min. The particle size at the optimum heat treatment condition for superior soft magnetic properties was found to be 6.0 -0.5 nm which was less compared than for the Fe-Nb-Cu-Si-B system. The observed coercivity value at the optimum heat treatment condition was found to be 0.32 A m m1 (approximately 4 mOe). The presence of Al in the alloy reduced the particle size and the magnetic anisotropy energy of the system, which resulted in superior soft magnetic properties of the heat-treated materials.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.