Abstract
The aim of this study was to compare the difference in bone formation between hydroxyapatite (HAp) and β-tricalcium phosphate (β-TCP) ceramics with similar porous structure. Porous HAp and β-TCP ceramics (total porosity: ~70%) with highly-interconnected structure were fabricated by firing calcium-phosphate fiber mixed with carbon beads (~150 μm). The size of highly-interconnected pores was measured by mercury intrusion technique. Each sample (ϕ4 mm × 8 mm) was implanted into the tibial bone defect (ϕ4.2 mm × 8 mm) of a pig (2 years old, male). After 6 weeks of implantation, undecalcified section was prepared and stained with hematoxylin and eosin (HE) stain. New bone area and remaining material area were evaluated.Interconnection sizes of HAp and β-TCP ceramics were 23.0 µm and 15.6 µm, respectively. New bone area of β-TCP ceramics was significantly higher compared to HAp ceramics. Remaining material ratio was 77.1 ± 3.3% for β-TCP ceramics whereas HAp ceramics remained stable. Bone formation in HAp ceramics was inhomogeneous compared to β-TCP ceramics in HE stained section. Although the β-TCP ceramics interconnection size was smaller, higher resorption may have played a positive role in homogeneous bone formation. According to the result of the study, it is suggested that highly-interconnected porous ceramics made by β-TCP could be a suitable material for bone regeneration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.