Abstract
AbstractThis work describes the role of manganese (Mn) as a sintering aid for magnesium aluminate (MgAl2O4) nanoparticles. Mn‐doped MgAl2O4 nanoparticles, synthesized by coprecipitation method, showed increased surface area when contrasted to undoped MgAl2O4. Fast firing of compacted‐doped nanoparticles achieved high degree of densification at temperatures as low as 1100°C with very moderate grain growth, resulting in average sizes at the nanoscale (~60 nm). Differential scanning calorimetry was used to quantify the exothermic heat effects of sintering, which combined with quantitative microstructural evolution analysis enabled calculation of both surface and grain boundary energies. The results revealed that Mn effectively reduces the surface and grain boundary energies which led to dihedral angle broadening and consequently increased sintering stress. Experimental data also revealed a concomitant decrease in the activation energy of sintering with Mn doping which dropped from 644 kJ/mol for undoped MgAl2O4 to 285 kJ/mol, informing Mn acts as a sintering aid in a thermokinetic manner.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.