Abstract
Effect of glass addition on the low-temperature sintering and microwave dielectric properties of BaTi4O9-based ceramics were studied to develop the middle-k dielectric composition for the functional substrate of low-temperature co-fired ceramics. When 10 wt% of glass was added, sufficient densification was obtained and the relative density more than 98% was reached at the sintering temperature of 875∘C. The microwave dielectric properties were k = 32, Q × f = 9000 GHz, and tcf = 10 ppm/∘C. As the added amount of glass frit with base dielectric composition, phase changes from BaTi4O9 to BaTi5O11 and Ba4Ti13O30 was observed, which result in the modification of microwave dielectric properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.