Abstract
The Ba(Mg1/2W1/2)O3 (BMW)–x wt% LiF (x = 2.0, 4.0, 6.0, 8.0) ceramics were prepared by a conventional solid-state route. The effects of LiF addition on the sinterability, crystal structure, microstructures and microwave dielectric properties of BMW ceramics were investigated. With an amount of LiF addition, the sintering temperature of the ceramics was reduced to below 960 °C from 1550 °C without degradation of microwave dielectric properties, due to the enhancement of the apparent density at low temperature by liquid phase sintering. On this basis, TiO2 was used to adjust the temperature coefficient of resonant frequency, optimized microwave dielectric properties with εr = 20, Q×f = 48,000 GHz, and τf = 1.2 ppm/°C for 0.96 BMW–0.04 TiO2–4.0 wt% LiF composition. With low sintering temperature and good dielectric properties, these LiF-doped ceramics are promising materials for LTCC integration applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.