Low-Temperature Preparation of Porous Cordierite-Mullite Ceramics Using Rice Husk as Silica Source and Pore-Forming Agent

Abstract

Listen

Translate article

Si and C of rice rusk were used as silica source and pore-forming agent to prepare cordierite-mullite ceramics at 1380°C for 5 h soaking. The Nd2O3 additive was added to improve the sintering properties. The bending strength, porosity, and thermal expansion coefficient were measured. The composition was characterized by X-ray diffraction (XRD). The microstructures of the sintered samples were observed by scanning electron microscopy (SEM). The cordierite-mullite ceramic doped with 2% Nd2O3 have high prorosity and low thermal expansion coefficient, its bending strength reaches 20.55 MPa. The addition of Nd2O3 decreases the mullite formation temperature to 1200 °C