Abstract
The effect of LiBF4 on the low-temperature performance of a Li-ion cell was studied by using a 1:1:1 (wt) EC/DMC/DEC mixed solvent. The results show that the LiBF4-based electrolyte has a 2- to 3-fold lower ionic conductivity and shows rather higher freezing temperature compared with a LiPF6-based electrolyte. Owing to electrolyte freezing, cycling performance of the Li-ion cell using LiBF4 was significantly decreased when the temperature fell below –20 °C. However, impedance data show that at –20 °C the LiBF4 cell has lower charge-transfer resistance than the LiPF6 cell. In spite of the relatively lower conductivity of the LiBF4-based electrolyte, the cell based on it shows slightly lower polarization and higher capacity in the liquid temperature range (above –20 °C) of the electrolyte. This fact reveals that ionic conductivity of the electrolytes is not a limitation to the low-temperature performance of the Li-ion cell. Therefore, LiBF4 may be a good salt for the low-temperature electrolyte of a Li-ion cell if a solvent system that is of low freezing temperature, high solubility to LiBF4, and good compatibility with a graphite anode can be formulated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.