Abstract
Tensile and Charpy properties of low-activation ferritic steel, F82H irradiated up to 0.8 dpa at low temperature below 300°C were investigated. The helium effect on these properties was also investigated using the boron isotope doping method. Neutron irradiation increased yield stress accompanied with ductility loss, and it also shifted the ductile-to-brittle transition temperature (DBTT) from −50°C to 0°C. Boron-doped F82H showed larger degradation in DBTT and ductility than boron-free F82H, while they had the same yield stress before and after irradiation.