Irradiation response on mechanical properties of neutron irradiated F82H

Abstract

Tensile and Charpy impact properties of neutron irradiated F82H (Fe8Cr2WVTa) with and without boron have been investigated to obtain the basic irradiation response on mechanical properties in low damage regime less than 1 dpa at the temperature ranging from 300° to 590°C. Boron-doped steel was used for the helium effect due to (n, α) reaction. Typical irradiation hardening was observed at 300°C. The irradiation above 520°C did not reveal increase in yield stress, but the specimen irradiated at 590°C showed some reduction in elongation in room temperature tensile testing. Slight difference in the tensile properties between boron-doped and boron-free were observed at 590°C. No changes in ductile brittle transition temperature (DBTT) occurred at a temperature between 335° and 460°C by Charpy impact testing.