Abstract
In this study, Zn8B3H3O14 nanosheets were synthesized through a one-step coprecipitation process and employed as both a boron source and substrate templates for the fabrication of boron nitride nanosheets (BNNSs), which were synthesized efficiently at low temperatures by the borate nitration method using ammonia as the nitrogen source. The thickness of the synthesized BNNSs ranged from 3 to 10 nm with a flake dimension of about 2.56 μm. The prepared BNNSs using this method realized 98.8% boron source utilization and single batch yields up to gram level. In addition, BNNSs/SiO2 microwave-transparent composites were prepared to investigate the potential for large-scale applications of the BNNSs produced by using this method. The composites demonstrated a remarkable increase in bending strength and fracture toughness, reaching 122.02 MPa and 2.31 MPa·m1/2, respectively, with the addition of only 0.5 wt% BNNSs. Compared with SiO2 without BNNSs, the fracture toughness of the composites is increased by 106%. A novel crack plugging strong toughening mechanism of BNNSs is proposed. Simultaneously, the composites exhibit exceptional microwave-transparent properties, with dielectric constants below 4 in the real part and below 0.03 in the imaginary part. Therefore, this study has successfully achieved the low-temperature and efficient synthesis of micron-scale BNNSs, laying the groundwork for their large-scale application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.