Abstract
AbstractEffects of low energy ion beam induced damages on transport properties of a two-dimensional electron gas (2DEG) system in GaAs/AlGaAs heterostructures have been investigated. 1 keV Ar ions were irradiated on the sample surface at several ion doses (1011 - 1013 cm-2). Carrier density and electron mobility of the 2DEG formed at about 90 nm below the GaAs/AlGaAs heterostructure surface were estimated at 1.5 K by Hall resistance and longitudinal resistance measurements before and after annealing at 400°C for 10 min in an Ar gas ambient. The temperature dependence of those values was also measured for as-grown and for 1013 cm-2 ion irradiated and subsequently annealed samples. Typical results show that carrier density and mobility are not degraded severely by Ar ion irradiation at doses of 1013 cm-2 and suggest the possibility to fabricate buried structures in GaAs/AlGaAs heterostructures using low energy Si focused ion beam (FIB) irradiation and subsequent in situ overlayer growth by MBE.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.