Abstract
Effects of low energy 30keV electron irradiation of superconducting YBa2Cu3O7−δ thin films have been investigated by means of transport and micro-Raman spectroscopy measurements. The critical temperature and the critical current of 200nm thick films initially increase with increasing fluency of the electron irradiation, reach the maximum at fluency 3−4×1020 electrons/cm2, and then decrease with further fluency increase. In much thinner films (75nm), the critical temperature increases while the critical current decreases after low energy electron irradiation with fluencies below 1020 electrons/cm2. The Raman investigations suggest that critical temperature increase in irradiated films is due to healing of broken CuO chains that results in increased carrier’s concentration in superconducting CuO2 planes. Changes in the critical current are controlled by changes in the density of oxygen vacancies acting as effective pinning centers for flux vortices. The effects of low energy electron irradiation of YBCO turned out to result from a subtle balance of many processes involving oxygen removal, both by thermal activation and kick-off processes, and ordering of chains environment by incident electrons.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.