Abstract
1 mol% Li 2O excess (Na 0.51K 0.47Li 0.02)(Nb 0.8Ta 0.2)O 3 ceramics were prepared by the conventional mixed oxide method and sintered from 950 to 1200 °C. Also, Li 2O was employed as a sintering aid for high densification and low temperature sintering process. X-ray diffraction results of 1 mol% Li 2O excess (Na 0.51K 0.47Li 0.02)(Nb 0.8Ta 0.2)O 3 lead free piezoelectric ceramics indicated that the specimens were well crystallized and have tetragonal structure. The specimens which sintered at 1050 °C showed the highest piezoelectric properties compared with others. The measured piezoelectric constant and electromechanical coupling coefficient were 231 pC/N and 38.9%, respectively. Curie temperature of (Na 0.51K 0.47Li 0.02)(Nb 0.8Ta 0.2)O 3 ceramics was 344.32, 344.4 and 344.5 °C at 1, 10 and 100 kHz, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.