Abstract
Focused ion beam sample preparation for transmission electron microscopy (TEM) can induce relaxation mechanisms in epitaxial thin films. Here, we describe a relaxation mechanism that can occur in materials having a tetragonal structure. We investigated the lattice structure of a 600 nm thick 0.4[Pb(Mg1/3Nb2/3)O3]−0.6[PbTiO3] layer grown by epitaxy on (110) GdScO3 substrate using geometrical phase analysis applied to high resolution TEM images. The lattice mismatch at the interface is expected to favor the formation of c-domains. However, it was measured that the out-of-plane lattice parameter can decrease abruptly along the growth direction and the transition depends on the thickness of the TEM lamella. Different observations indicate that the crystal flipped by 90° following the preparation of the sample, so that the c-axis is oriented in the thinning direction. Such a mechanism can easily lead to misinterpretations and might happen in other materials with a similar structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.