Abstract
The morphology and crystallography of M2C carbide precipitates in the ferrite matrix in M50NiL alloy were investigated using transmission electron microscopy (TEM). A new orientation relationship (OR), (010)α // \((01\bar 11)_C \) and [100]α // \((2\overline {11} 0)_C \) between the carbide and the matrix was determined. The observed OR leads to a small lattice misfit on the matching planes between the two phases. Results of TEM studies of the particle morphology and electron diffraction of the carbide are consistent with the proposed OR.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.