Abstract
A 180-nm-thick boron (B) layer was deposited on a 300-nm-thick a-axis-oriented BaSi2 epitaxial film grown by molecular beam epitaxy on Si(111) and was annealed at different temperatures in ultrahigh vacuum. The depth profiles of B were investigated using secondary ion mass spectrometry (SIMS) with O2+, and the diffusion coefficients of B were evaluated. The B profiles were reproduced well by taking both the lattice and the grain boundary (GB) diffusions into consideration. The cross-sectional transmission electron microscopy (TEM) image revealed that the GBs of the BaSi2 film were very sharp and normal to the sample surface. The plan-view TEM image exhibited that the grain size of the BaSi2 film was approximately 0.6 μm. The temperature dependence of lattice and GB diffusion coefficients was derived from the SIMS profiles, and their activation energies were found to be 4.6 eV and 4.4 eV, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.