Abstract
Deep level transient spectroscopy (DLTS) and deep level optical spectroscopy (DLOS) measurements have been carried out in neutron-irradiated n-type hydride-vapor-phase-epitaxy-grown GaN. A defect center characterized by a DLTS line, labeled as N1, is observed at EC−ET=0.17eV. Another line, labeled as N2, at EC−ET=0.23eV, seems to be induced at the same rate as N1 under irradiation and may be identified with E1. Other defects native to wurtzite GaN such as the C and E2 lines appear to enhance under neutron irradiation. The DLOS results show that the defects N1 and N2 have large Frank-Condon shifts of 0.64 and 0.67eV, respectively, and hence large lattice relaxations. The as-grown and neutron-irradiated samples all exhibit the persistent photoconductivity effect commonly seen in GaN that may be attributed to DX centers. The concentration of the DX centers increases significantly with neutron dosage and is helpful in sustaining sample conductivity at low temperatures, thus making possible DLTS measurements on N1 an N2 in the radiation-induced deep-donor defect compensated material which otherwise are prevented by carrier freeze-out.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call