Lamb wave propagation in Z-pin reinforced co-cured composite pi-joints

Abstract

Listen

Translate article

This paper presents an initial study on Lamb wave propagation characteristics in z-pin reinforced, co-cured composite pi-joints for the purposes of structural health monitoring (SHM). Pi-joint test articles were designed and created to replicate a co-cured, all composite skin-spar joint found within a typical aircraft wing structure. Because pi-joints exhibit various complex damage modes, formal studies are required if SHM systems are to be developed to monitor these types of joints for potential damage. Experiments were conducted on a undamaged (healthy) and damaged test articles where Lamb waves were excited using one lead zirconate titanate (PZT) transducer. A three-dimensional (3D) scanning laser Doppler vibrometer (LDV) was used to collect high-density scans of both the in-plane and out-of-plane velocity measurements. In the damaged test article, where delamination, matrix cracking, and fiber breakage can clearly be seen, changes in both the fundamental antisymmetric A0 and symmetric S0 Lamb wave modes are apparent. In both test articles, the effects of narrow geometry, discontinuity due to the attachment of the web, and thickness has detectable effects on Lamb wave propagation. From the comparisons between Lamb waves propagating through the undamaged and damaged test articles, it is clear that damage can be detected using Lamb waves in z-pin reinforced, co-cured composite pi-joints for this case of extensive damage.