Kinetics of the formation of a diffusion layer on AISI 1045 steel with simultaneous saturation with boron, chromium and titanium

Abstract

Research has been carried out to determine the kinetics of coating formation on AISI 1045 steel with diffusion saturation with boron, chromium and titanium simultaneously. It was found that the experimental parameters of the thickness of the diffusion layer of borides over time outstrip the calculated values. The diffusion layer has a thickness of 120 μm with a saturation duration of 2.5 h, 155 μm with a saturation duration of 5 h, and 180 μm with a saturation duration of 7.5 h. In addition to studying the kinetics of the formation of a diffusion coating, also studied the distribution of microhardness over the cross section of the diffusion coating. The maximum microhardness of the diffusion coating is observed not on the surface, but at some distance from it. On average, at a depth of 45–60 µm from the surface. In this case, the microhardness on the surface of the diffusion coating, on the contrary, tends to take on a minimum value of about 1800 HV0.1. Such a distribution of microhardness it gives the parts the possibility of minor surface wear.