Abstract
Ferromagnetic L10 MnAl phase was achieved in as-grown MnAl alloy thin films by using 250 keV H+ ion irradiation without conventional post annealing. The magnetic properties and crystallinity of MnAl thin film got modified with increase in irradiation fluence. The magnetic coercivity was found to be maximum (2500 Oe) at the fluence of 5 × 1014 ions cm−2. The hysteresis curve for the sample irradiated by H+ ions with fluence of 5 × 1016 ions cm−2 exhibited highest saturation magnetization (130 emu/cc) among all irradiated films. The increase in irradiation fluence led to larger grain growth as confirmed from AFM results. The magnetic domain pattern observed by MFM images confirmed the presence of ferromagnetic τ-phase in irradiated samples. The present study establishes that the H+ ion-irradiation can be an effective technique to tailor the structural as well as magnetic properties of MnAl thin films.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.