Ion sputtering rates of W-, Ti- and Cr-carbides studied at different Ar + ion incidence angles

Abstract

To study the ion sputtering rates of W-, Ti- and Cr-carbides, trilayer structures comprising C-graphite (59 nm)/WC (50 nm)/W (38 nm), C-graphite (56 nm)/TiC (40 nm)/Ti (34 nm) and C-graphite (46 nm)/C 3C 2 (60 nm)/Cr (69 nm) with a tolerance ±2% were sputter deposited onto smooth silicon substrates. Their precise structural and compositional characterization by transmission electron microscopy (TEM), Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) revealed that the WC and Cr 3C 2 layers were amorphous, while the TiC layer had a polycrystalline structure. The ion sputtering rates of all three carbides, amorphous carbon and polycrystalline Cr, Ti and W layers were determined by means of Auger electron spectroscopy depth profiling as a function of the angle of incidence of two symmetrically inclined 1 keV Ar + ion beams in the range between 22° and 82°. The sputtering rates were calculated from the known thicknesses of the layers and the sputtering times necessary to remove the individual layers. It was found that the sputtering rates of carbides, C-graphite and metals were strongly angle dependent. For the carbides in the range between 36° and 62° the highest ion sputtering rate was found for Cr 3C 2 and the lowest for TiC, while the values of the sputtering rates for WC were intermediate. The normalized sputtering yields calculated from the experimentally obtained data for all three carbides followed the trend of theoretical results obtained by calculation of the transport of ions in solids by the SRIM code. The sputtering yields are also presented in terms of atoms/ion. Our experimental data for two ion incidence angles of 22° and 49° and reported values of other authors for C-graphite and metals are mainly inside the estimated error of about ±20%. The influence of the ion-induced surface topography on the measured sputtering yields was estimated from the atomic force microscope (AFM) measurements at the intermediate points of the corresponding layers on the crater walls formed during depth profiling.